PMMA-Like Transparent Resin
AcryGlo6000 is a transparent SLA resin for fast, precise, and clear parts with an acrylic-like finish.
Excellent transparency
Excellent humidity and moisture resistance
Fast to build and easy to finish
Accurate and dimensionally stable
Liquid Properties
| Color | Transparent and Clear |
| Density (g/cm³) | 1.1q-1.14g/cm³ @ 25℃ |
| Viscosity | 325-425 cps @ 28℃ |
Optical Properties
| Dp | 0.135-0.155 mm |
| Ec | 9-12 mJ/cm² |
| Building Layer Thickness | 0.1-0.15mm |
Mechanical Properties
| Hardness, Shore D | ASTM D 2240 | 72-78 |
| Flexural Modulus, Mpa | ASTM D 790 | 2680-2775 |
| Flexural Strength, Mpa | ASTM D 790 | 65-75 |
| Tensile Modulus, Mpa | ASTM D 638 | 2170-2385 |
| Tensile Strength, Mpa | ASTM D 638 | 25-30 |
| Elongation at Break | ASTM D 638 | 12 -20% |
| lmpact Strength, notched lzod, J/m | ASTM D 256 | 58 -70 |
| Heat Delection Temperature, ℃ | ASTM D 648 @66PS | 50-60 |
| Glass transition, Tg ℃ |
DMA，E”peak | 55-70 |
| Density, g/cm3 | 1.14-1.16 |